Rueda Sánchez, Juan CarlosRengifo Maravi, Joel Claudio2018-09-042018-09-0420182018-09-04http://hdl.handle.net/20.500.12404/12576La presente tesis trata sobre la síntesis y caracterización de los hidrogeles interpenetrados (IPN) sensibles a la temperatura y al pH, compuestos por una primera red polimérica basada en N-isopropilacrilamida (NiPAAm) (termosensible) y una segunda red polimérica basada en macromonómero de 2-oxazolina y acrilamida (sensible al pH). Estos hidrogeles IPN se sintetizan en tres etapas. Primeramente, se sintetiza el hidrogel de NiPAAm por polimerización radicalaria de una solución acuosa de NiPAAm en presencia de la N,N’-metil-bisacrilamida (BIS) como agente entrecruzante. Después se sintetiza la segunda red polimérica mediante una polimerización radicalaria de la acrilamida y un macromonómero de 2-oxazolina (MM), el cual es un copolímero estadístico de 2-metil-2-oxazolina (MeOXA) y 2-carboxietil-2-oxazolina (EsterOXA), en presencia de la primera red polimérica de NiPAAm. Finalmente, se realiza la hidrólisis básica de los grupos ésteres presentes en el hidrogel IPN. Se caracteriza al hidrogel IPN por diferentes métodos. La absorción de agua y la sensibilidad del hidrogel IPN a diferentes pH y temperaturas se determina mediante el peso de los hidrogeles en diferentes condiciones. La caracterización estructural se realiza por espectroscopia infrarroja con transformada de Fourier (FTIR) mediante la técnica de reflectancia total atenuada (ATR) y por resonancia magnética nuclear de protón (1H-RMN) en el modo de alta resolución con ángulo mágico (HR-MAS). Su comportamiento mecánico se estudia mediante el análisis mecánico dinámico de compresión (AMC). La caracterización estructural demuestra la formación del hidrogel IPN. La sensibilidad a la temperatura del hidrogel IPN se debe a la presencia del PoliNiPAAm, conforme aumenta la cantidad molar del NiPAAm, disminuye la temperatura de transición conformacional, aumentando la contracción del hidrogel. Mientras que la sensibilidad al pH del hidrogel IPN se debe a la presencia de los grupos carboxilatos de la segunda red polimérica, el hidrogel a pH bajos se contrae y a pH altos se expande.The present thesis is about the synthesis and characterization of interpenetrated polymer network (IPN) hydrogels of sensitive temperature and sensitive pH, composed of a first polymer network based on N-isopropylacrylamide (NiPAAm) (thermosensitive) and a second polymer network based on macromonomer of 2-oxazoline and acrylamide (ph sensitive). These IPN hydrogels are synthesized in three steps. Firstly, the NiPAAm hydrogel is synthesized by free radical polymerization in an aqueous NiPAAm solution in presence of N,N´-methyl-bisacrylamide (BIS) as crosslinking agent. After the second polymer network is synthesized by free radical polymerization of acrylamide and macromonomer (MM) of 2-oxazoline, which is a statistical copolymer of 2-methyl-2- oxazoline (MeOXA) and 2-carboxyethyl-2-oxazoline. (EsterOXA), in the presence of the first NiPAAm polymer network. Finally, the ester groups present in the IPN hydrogel is hydrolyzed. The IPN hydrogel is characterized by different methods. Hydrogel swelling and the sensitivity of the IPN hydrogel at different pH and temperatures is determined by the weight of the hydrogels under different conditions. The structural characterization by Fourier transform infrared spectroscopy (FTIR) the technique of attenuated total reflectance (ATR) and proton nuclear magnetic resonance (1H-RMN) by highresolution magic-angle-spinning (HR-MAS). The mechanical behavior is studied through dynamic mechanical analysis (DMA). The structural characterization demonstrates formation of the IPN hydrogel. The sensitivity to temperature of the IPN hydrogel is due to presence of PoliNiPAAm, just as the molar amount of NiPAAm increases, decreases the conformational transition temperature; raise the contraction of the hydrogel. While the pH sensitivity of the IPN hydrogel is due to presence of the carboxylate groups of the second polymer network, at down pH the hydrogel contracts and at high pH the hydrogel expands.spainfo:eu-repo/semantics/openAccesshttp://creativecommons.org/licenses/by-nc-nd/2.5/pe/HidrogelesResonancia magnética nuclearPolímerosinfo:eu-repo/semantics/masterThesishttps://purl.org/pe-repo/ocde/ford#1.04.00